牌号简介 About |
---|
Amodel AS -1133 HS是33%玻纤增强热稳定型聚邻苯二甲酰胺(PPA)树脂,即使是那些壁厚大于0.125英寸( 3毫米)的成型部件,也具有优异的结构完整性 。 该结构性树脂的主要特性包括高热变形温度、高挠曲模量、高拉伸强度、优良的耐蠕变性和低吸湿性。 - 黑色:AS-1133 HS BK 324 本色: AS-1133 HS NT Amodel® AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0.125 in (3 mm). Key properties of this structural resin are high heat deflection temperature, high flexural modulus, high tensile strength, excellent creep resistance and low moisture absorption. Black: AS-1133 HS BK 324 Natural: AS-1133 HS NT |
产品描述 Product Description
厂家:比利时索尔维 Solvay Engineering Plastics
类别:PPA PPA
用途:机器/机械部件;连接器;动力/其它工具;金属取代;燃料管线;外壳;阀门/阀门部件;石油/天然气用品;草坪和园林设备;汽车领域的应用;厚壁配件(部件);工业应用;通用;工业部件;汽车电子;汽车的发动机罩下的零件;
颜色:黑色,自然色
加工条件:注射成型 Injection Molding
性能特点:防火阻燃等级HB; 低吸湿性; 热稳定性好; 机械强度好; 尺寸稳定性好; 耐化学性; 耐高温; 韧性好; Good Rigidity,Good flexibility,Good Dimensional Stability,High Heat Resistance,Solvent resistance,Low moisture absorption,Heat Stabilized,HB
填料:玻璃纤维 33
技术参数 Technical Data | |||
---|---|---|---|
物理性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
密度 Density | 1.44 | g/cm³ | ISO 1183/B |
收缩率 收缩率 | |||
TD TD | 0.80 | % | ASTM D955 |
MD MD | 0.40 | % | ASTM D955 |
吸水率 吸水率 | |||
24hr 24 hr | 0.21 | % | ASTM D570 |
冲击性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength | 11 | kJ/m² | ISO 179-1eA |
简支梁无缺口冲击强度 Charpy Unnotched Impact Strength | 82 | kJ/m² | ISO 179/1eU |
悬臂梁缺口冲击强度 Notched Izod Impact Strength | 85 | J/m | ASTM D256 |
悬臂梁缺口冲击强度 Notched Izod Impact Strength | 11 | kJ/m² | ISO 180-1A |
悬臂梁缺口冲击强度 Notched Izod Impact Strength | 1000 | J/m | ASTM D256 |
热性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
热变形温度 热变形温度 | |||
1.8 MPa,退火,3.18 mm 1.8 MPa,退火,3.18 mm | 285 | ℃ | ASTM D648 |
1.8 MPa,退火 1.8 MPa,退火 | 277 | ℃ | ISO 75-2/Af |
0.45 MPa,退火,3.2 mm 0.45 MPa,退火,3.18 mm | 297 | ℃ | ASTM D648 |
连续使用温度 Continuous Use Temperature | ASTM D3045 | ||
-- -- 2 2 | 164 | ℃ | ASTM D3045 |
-- -- 3 3 | 185 | ℃ | ASTM D3045 |
熔融峰值温度 Peak Melting Temperature | 310 | ℃ | ASTM D3418 |
熔融温度 Melting Temperature | 310 | ℃ | ISO 11357-3 |
线性热膨胀系数 线性热膨胀系数 | |||
TD TD | ASTM E831 | ||
0 到 100℃ 0 to 100°C | 5.9E-5 | cm/cm/℃ | ASTM E831 |
160 到 249℃ 160 to 249°C | 1.3E-4 | cm/cm/℃ | ASTM E831 |
MD MD | ASTM E831 | ||
0 到 100℃ 0 to 100°C | 2.3E-5 | cm/cm/℃ | ASTM E831 |
160 到 249℃ 160 to 249°C | 1.4E-5 | cm/cm/℃ | ASTM E831 |
电气性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
体积电阻率 Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
介电强度 介电强度 | |||
3.18 mm 3.17 mm | 21 | kV/mm | ASTM D149 |
介电常数 Dielectric Constant | ASTM D150 | ||
60 Hz 60 Hz | 4.40 | ASTM D150 | |
1 MHz 1 MHz | 4.20 | ASTM D150 | |
耗散因数 Dissipation Factor | ASTM D150 | ||
60 Hz 60 Hz | 5.0E-3 | ASTM D150 | |
1 MHz 1 MHz | 0.017 | ASTM D150 | |
耐电弧性 Arc Resistance | 140 | sec | ASTM D495 |
相比漏电起痕指数 Comparative Tracking Index (CTI) | 550 | V | UL 746 |
阻燃性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
阻燃等级 3.2 mm 4 | |||
3.20 mm | HB | UL 94 | |
光学性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
透光率 Transmittance 5 5 | ASTM D1003 | ||
1070 nm,1.60 mm 1070 nm : 1.60 mm | > 35 | % | ASTM D1003 |
1.60 mm,940 nm 940 nm : 1.60 mm | > 30 | % | ASTM D1003 |
机械性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
拉伸模量 Tensile Modulus | 13100 | MPa | ASTM D638 |
拉伸模量 Tensile Modulus | 12200 | MPa | ISO 527-2 |
拉伸强度 拉伸强度 | |||
断裂 断裂 | 221 | MPa | ASTM D638 |
屈服 屈服 | 225 | MPa | ISO 527-2 |
拉伸应变 拉伸应变 | |||
断裂 断裂 | 2.5 | % | ASTM D638 |
断裂 断裂 | 3.0 | % | ISO 527-2 |
弯曲模量 Flexural Modulus | 10300 | MPa | ASTM D790 |
弯曲模量 Flexural Modulus | 10300 | MPa | ISO 178 |
弯曲强度 Flexural Stress | 326 | MPa | ISO 178 |
屈服 屈服 | 317 | MPa | ASTM D790 |
压缩强度 Compressive Strength | 276 | MPa | ASTM D695 |
剪切强度 Shear Strength | 101 | MPa | ASTM D732 |
泊松比 Poisson's Ratio | 0.41 | ASTM E132 | |
洛氏硬度 洛氏硬度 | |||
R 级 R 级 | 125 | ASTM D785 |
分享到: