牌号简介 About |
---|
AMODEL AS -1933 HS是33%玻纤增强级聚邻苯二甲酰胺(PPA)树脂,专门为了改善产品在50/50乙二醇和水环境中的性能而开发。此材料在226°F(108 ℃), 甚至在275 °F(135 ℃)测试温度下暴露于抗冻结剂时,性能超过汽车行业对聚合物材料的要求。 可用于各种汽车零部件,如节温器壳体、加热器核心端盖、加热器软管接头和进水口、电源插座及阀门灯。 - 黑色: AS-1933 HS BK 324 Amodel® AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226°F (108°C), even when tested at 275°F (135°C). Potential applications include a variety of automotive components such as thermostat housings, heater core endcaps, heater hose connectors, and water inlets, outlets and valves. Black: AS-1933 HS BK 324 |
产品描述 Product Description
厂家:比利时索尔维 Solvay Engineering Plastics
类别:PPA PPA
用途:阀门/阀门部件;汽车领域的应用;厚壁配件(部件);机器/机械部件;工业应用;工业部件;动力/其它工具;金属取代;外壳;汽车的发动机罩下的零件;
颜色:黑色
加工条件:注射成型 Injection Molding
性能特点:热稳定性好; 机械强度好; 尺寸稳定性好; 耐乙二醇; 耐化学性; 耐高温; 耐低温; 韧性好; Good Rigidity,Ethylene glycol,Good flexibility,Good Dimensional Stability,Antifreeze,High Heat Resistance,Solvent resistance,Heat Stabilized
填料:玻璃纤维 33
技术参数 Technical Data | |||
---|---|---|---|
物理性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
密度 Density | 1.45 | g/cm³ | ISO 1183/A |
收缩率 Molding Shrinkage | ASTM D955 | ||
MD 流动 | 0.20 | % | |
TD 横向流动 | 0.60 | % | |
吸水率 吸水率 | |||
24hr 24 hr | 0.21 | % | ASTM D570 |
机械性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
拉伸模量 Tensile Modulus | |||
-- -- 1 1 | 7580 | MPa | ASTM D638 |
-- -- | 11700 | MPa | ASTM D638 |
-- -- | 12600 | MPa | ISO 527-2 |
拉伸强度 Tensile Strength | |||
断裂 断裂 2 2 | 75.8 | MPa | ASTM D638 |
断裂 Break | 221 | MPa | ASTM D638 |
断裂 Break | 212 | MPa | ISO 527-2 |
拉伸应变 拉伸应变 | |||
断裂 断裂 | 2.5 | % | ASTM D638, ISO 527-2 |
弯曲模量 Flexural Modulus | |||
-- -- | 10800 | MPa | ASTM D790 |
-- -- | 10600 | MPa | ISO 178 |
弯曲强度 Flexural Stress | |||
-- -- | 309 | MPa | ISO 178 |
屈服 Yield | 313 | MPa | ASTM D790 |
冲击性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179-1eA |
简支梁无缺口冲击强度 Charpy Unnotched Impact Strength | 76 | kJ/m² | ISO 179/1eU |
悬臂梁缺口冲击强度 Notched Izod Impact Strength | |||
-- -- 3 3 | 53 | J/m | ASTM D256 |
-- -- | 91 | J/m | ASTM D256 |
-- -- | 9.5 | kJ/m² | ISO 180-1A |
热性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
热变形温度 Deflection Temperature Under Load | |||
1.8 MPa,未退火 264 psi, Unannealed | 277 | ℃ | ASTM D648 |
1.8 MPa,未退火 264 psi, Unannealed | 278 | ℃ | ISO 75-2/Af |
熔融温度 Melting Temperature | 312 | ℃ | ISO 11357-3 |