1/0
| 牌号简介 About |
|---|
| Amodel AS- 4133 HS是33％玻纤增强、润滑、热稳定型聚邻苯二甲酰胺（PPA ），可快速加工、在水温模具中成型。常规应用包括电气和电子元件，尤其是汽车系统用电子电气元件。 - 黑色：AS-4133 HS BK 324 本色： AS-4133 HS NT Amodel® AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Testing conducted on samples dry as molded and samples conditioned to 50% relative humidity in accordance with ISO-1110, Accelerated Method. Typical applications include electrical and electronic components especially for automotive systems. Black: AS-4133 HS BK 324 Natural: AS-4133 HS NT |
产品描述 Product Description
厂家：比利时索尔维 Solvay Engineering Plastics
类别：PPA PPA
用途：电气/电子应用领域;机器/机械部件;连接器;金属取代;阀门/阀门部件;手机;草坪和园林设备;厚壁配件（部件）;汽车领域的应用;工业应用;通用;工业部件;汽车电子;汽车的发动机罩下的零件;
颜色：自然色,黑色
加工条件：水温模具注塑成型
性能特点：低吸湿性; 防火阻燃等级HB; 热稳定性好; 机械强度好; 激光加工-焊接; 尺寸稳定性好; 成型周期快; 耐化学性; 耐高温; 润滑性; 韧性好; Good Rigidity,Good flexibility,Good Dimensional Stability,Quick molding cycle,Laser welding,High Heat Resistance,Lubricating,Solvent resistance,Low moisture absorption,Heat Stabilized,HB
填料：玻璃纤维 33
| 技术参数 Technical Data | |||
|---|---|---|---|
物理性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 密度 Density | 1.45 | g/cm³ | ISO 1183/A |
| 收缩率 收缩率 | |||
| TD TD | 1.0 | % | ASTM D955 |
| MD MD | 0.50 | % | ASTM D955 |
| 吸水率 吸水率 | |||
| 24hr 24 hr | 0.29 | % | ASTM D570 |
机械性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 拉伸模量 Tensile Modulus | 11700 | MPa | ASTM D638 |
| 拉伸模量 Tensile Modulus | ISO 527-2 | ||
| 23℃ 23°C | 12600 | MPa | ISO 527-2 |
| 100℃ 100°C | 6830 | MPa | ISO 527-2 |
| 150℃ 150°C | 5310 | MPa | ISO 527-2 |
| 175℃ 175°C | 4830 | MPa | ISO 527-2 |
| 拉伸强度 Tensile Strength | 200 | MPa | ASTM D638 |
| 拉伸强度 Tensile Stress | ISO 527-2 | ||
| 断裂，23℃ Break, 73°F | 211 | MPa | ISO 527-2 |
| 断裂，24℃ Break, 212°F | 125 | MPa | ISO 527-2 |
| 断裂，150℃ Break, 302°F | 87.6 | MPa | ISO 527-2 |
| 断裂，175℃ Break, 347°F | 79.3 | MPa | ISO 527-2 |
| 拉伸应变 Tensile Strain | ISO 527-2 | ||
| 断裂 断裂 | 2.5 | % | ASTM D638 |
| 断裂，23℃ Break, 73°F | 2.6 | % | ISO 527-2 |
| 断裂，24℃ Break, 212°F | 4.3 | % | ISO 527-2 |
| 断裂，150℃ Break, 302°F | 6.6 | % | ISO 527-2 |
| 断裂，175℃ Break, 347°F | 6.6 | % | ISO 527-2 |
| 弯曲模量 Flexural Modulus | 11000 | MPa | ASTM D790 |
| 弯曲模量 Flexural Modulus | ISO 178 | ||
| 23℃ 23°C | 10400 | MPa | ISO 178 |
| 100℃ 100°C | 7170 | MPa | ISO 178 |
| 150℃ 150°C | 4620 | MPa | ISO 178 |
| 175℃ 175°C | 4210 | MPa | ISO 178 |
| 弯曲强度 Flexural Strength | 290 | MPa | ASTM D790 |
| 弯曲强度 Flexural Stress | ISO 178 | ||
| 23℃ 23°C | 296 | MPa | ISO 178 |
| 100℃ 100°C | 177 | MPa | ISO 178 |
| 150℃ 150°C | 111 | MPa | ISO 178 |
| 175℃ 175°C | 99.3 | MPa | ISO 178 |
| 压缩强度 Compressive Strength | 179 | MPa | ASTM D695 |
| 剪切强度 Shear Strength | 89.6 | MPa | ASTM D732 |
| 泊松比 Poisson's Ratio | 0.41 | ASTM E132 | |
冲击性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 简支梁缺口冲击强度 简支梁缺口冲击强度 | |||
| 23℃ 23℃ | 11 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 简支梁无缺口冲击强度 | |||
| 23℃ 23℃ | 67 | kJ/m² | ISO 179/1eU |
| 悬臂梁缺口冲击强度 Notched Izod Impact Strength | 80 | J/m | ASTM D256 |
| 悬臂梁缺口冲击强度 Notched Izod Impact Strength | 960 | J/m | ASTM D256 |
| 23℃ 23℃ | 9.7 | kJ/m² | ISO 180-1A |
| 悬臂梁无缺口冲击强度 悬臂梁无缺口冲击强度 | |||
| 23℃ 23℃ | 59 | kJ/m² | ISO 180/1U |
热性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 热变形温度 热变形温度 | |||
| 1.8 MPa，退火，3.2 mm 1.8 MPa，退火，3.20 mm | 300 | ℃ | ASTM D648 |
| 1.8 MPa，未退火 1.8 MPa，未退火 | 294 | ℃ | ISO 75-2/A |
| 0.45 MPa，退火，3.2 mm 0.45 MPa，退火，3.20 mm | 320 | ℃ | ASTM D648 |
| 连续使用温度 Continuous Use Temperature 2 2 | 210 | ℃ | ASTM D3045 |
| 熔融温度 Melting Temperature | 327 | ℃ | ISO 11357-3 |
| 熔融温度 Melting Temperature | 327 | ℃ | ASTM D570 |
| 线性热膨胀系数 线性热膨胀系数 | |||
| TD TD | ASTM E831 | ||
| 0 到 100℃ 0 to 100°C | 7.6E-5 | cm/cm/℃ | ASTM E831 |
| 100 到 200℃ 212 to 392°F | 1.2E-4 | cm/cm/℃ | ASTM E831 |
| MD MD | ASTM E831 | ||
| 0 到 100℃ 0 to 100°C | 2.0E-5 | cm/cm/℃ | ASTM E831 |
| 100 到 200℃ 212 to 392°F | 1.5E-5 | cm/cm/℃ | ASTM E831 |
电气性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 体积电阻率 Volume Resistivity | 2.0E+16 | ohms·cm | ASTM D257 |
| 介电强度 介电强度 | |||
| 1.6 mm 1.60 mm | 20 | kV/mm | ASTM D149 |
| 介电常数 Dielectric Constant | ASTM D150 | ||
| 60 Hz 60 Hz | 3.80 | ASTM D150 | |
| 1 MHz 1 MHz | 3.60 | ASTM D150 | |
| 耗散因数 Dissipation Factor | ASTM D150 | ||
| 60 Hz 60 Hz | 4.0E-3 | ASTM D150 | |
| 1 MHz 1 MHz | 0.012 | ASTM D150 | |
| 相比漏电起痕指数 Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| 高电压电弧起痕速率 高电压电弧起痕速率 | |||
| HVTR HVTR | 14.0 | mm/min | UL 746 |
阻燃性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 阻燃等级 3.2 mm 3 | |||
| 3.20 mm | HB | UL 94 | |
光学性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 透光率 Transmittance 4 4 | ASTM D1003 | ||
| 1070 nm，1.60 mm 1070 nm : 1.60 mm | > 20 | % | ASTM D1003 |
| 1.60 mm，940 nm 940 nm : 1.60 mm | > 20 | % | ASTM D1003 |