| Amodel® A-6135 HN聚邻苯二甲酰胺（ppa）是一种35%的玻璃纤维增强树脂，具有热稳定、润滑和热水可塑性。该树脂的关键性能是在较宽的温度范围内具有较高的耐热性、高强度和刚度。它还具有低吸湿性、优异的耐化学性和优良的电气性能。Amodel® A-6135 HN树脂是理想的汽车电气和电子应用，包括连接器，插座，开关和传感器。它也是保护关键控制系统（如防抱死制动器、牵引力控制、转向、电子发动机控制、变速箱和底盘控制单元）的发动机罩下外壳的理想选择。黑色：A-6135 HN BK 324 Natural A-6135 HS NT Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, non-lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel® A-6135 HN resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Black: A-6135 HN BK 324 |
产品描述 Product Description
厂家：比利时索尔维 Solvay Engineering Plastics
类别：PPA PPA
用途：电器外壳;电气/电子应用领域;机器/机械部件;连接器;动力/其它工具;金属取代;外壳;阀门/阀门部件;草坪和园林设备;汽车领域的应用;工业应用;通用;工业部件;汽车电子;汽车的发动机罩下的零件;
颜色：黑色
加工条件：水温模具注塑成型
性能特点：低吸湿性; 热稳定性好; 机械强度好; 耐化学性; 耐高温; 易流动; 韧性好; Good Rigidity,Good flexibility,Good liquidity,High Heat Resistance,Solvent resistance,Low moisture absorption,Heat Stabilized
填料：玻璃纤维 35
| 技术参数 Technical Data | |||
|---|---|---|---|
物理性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 密度 Density | 1.45 | g/cm³ | ISO 1183/A |
| 收缩率 Molding Shrinkage | ISO 294-4 | ||
| TD TD | 0.90 | % | ASTM D955 |
| MD MD | 0.60 | % | ASTM D955 |
| TD Across Flow | 1.0 | % | ISO 294-4 |
| MD Flow | 0.50 | % | ISO 294-4 |
| 吸水率 吸水率 | |||
| 24hr 24 hr | 0.30 | % | ASTM D570 |
| 23℃，24hr 23℃，24 hr | 0.29 | % | ISO 62 |
冲击性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 简支梁缺口冲击强度 简支梁缺口冲击强度 | |||
| 23℃ 23℃ | 9.2 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 简支梁无缺口冲击强度 | |||
| 23℃ 23℃ | 60 | kJ/m² | ISO 179/1eU |
| 悬臂梁缺口冲击强度 Notched Izod Impact Strength | 85 | J/m | ASTM D256 |
| 23℃ 23℃ | 9.1 | kJ/m² | ISO 180 |
| 悬臂梁缺口冲击强度 Notched Izod Impact Strength | 800 | J/m | ASTM D256 |
| 悬臂梁无缺口冲击强度 悬臂梁无缺口冲击强度 | |||
| 23℃ 23℃ | 62 | kJ/m² | ISO 180 |
热性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 热变形温度 热变形温度 | |||
| 1.8 MPa，退火，3.2 mm 1.8 MPa，退火，3.20 mm | 291 | ℃ | ASTM D648 |
| 1.8 MPa，未退火 1.8 MPa，未退火 | 288 | ℃ | ISO 75-2/A |
| 0.45 MPa，未退火 0.45 MPa，未退火 | 303 | ℃ | ISO 75-2/B |
| 熔融温度 Melting Temperature | 310 | ℃ | ISO 11357-3 |
| 熔融温度 Melting Temperature | 310 | ℃ | ASTM D570 |
| 线性热膨胀系数 线性热膨胀系数 | |||
| TD TD | ASTM E831 | ||
| 0 到 100℃ 0 to 100°C | 6.1E-5 | cm/cm/℃ | ASTM E831 |
| 100 到 200℃ 212 to 392°F | 1.0E-4 | cm/cm/℃ | ASTM E831 |
| MD MD | ASTM E831 | ||
| 0 到 100℃ 0 to 100°C | 2.2E-5 | cm/cm/℃ | ASTM E831 |
| 100 到 200℃ 212 to 392°F | 1.6E-5 | cm/cm/℃ | ASTM E831 |
机械性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 拉伸模量 Tensile Modulus | 13800 | MPa | ASTM D638 |
| 拉伸模量 Tensile Modulus | ISO 527-2 | ||
| 23℃ 23°C | 11500 | MPa | ISO 527-2 |
| 100℃ 100°C | 7310 | MPa | ISO 527-2 |
| 150℃ 150°C | 6270 | MPa | ISO 527-2 |
| 175℃ 175°C | 5310 | MPa | ISO 527-2 |
| 拉伸强度 Tensile Strength | 203 | MPa | ASTM D638 |
| 拉伸强度 Tensile Stress | ISO 527-2 | ||
| 断裂，23℃ Break, 73°F | 211 | MPa | ISO 527-2 |
| 断裂，24℃ Break, 212°F | 121 | MPa | ISO 527-2 |
| 断裂，150℃ Break, 302°F | 92.4 | MPa | ISO 527-2 |
| 断裂，175℃ Break, 347°F | 82.0 | MPa | ISO 527-2 |
| 拉伸应变 Tensile Strain | ISO 527-2 | ||
| 断裂 断裂 | 1.9 | % | ASTM D638 |
| 断裂，23℃ Break, 73°F | 2.0 | % | ISO 527-2 |
| 断裂，24℃ Break, 212°F | 4.3 | % | ISO 527-2 |
| 断裂，150℃ Break, 302°F | 4.9 | % | ISO 527-2 |
| 断裂，175℃ Break, 347°F | 4.7 | % | ISO 527-2 |
| 弯曲模量 Flexural Modulus | 11400 | MPa | ASTM D790 |
| 弯曲模量 Flexural Modulus | ISO 178 | ||
| 23℃ 23°C | 11400 | MPa | ISO 178 |
| 100℃ 100°C | 6600 | MPa | ISO 178 |
| 150℃ 150°C | 4900 | MPa | ISO 178 |
| 175℃ 175°C | 4600 | MPa | ISO 178 |
| 弯曲强度 Flexural Strength | 310 | MPa | ASTM D790 |
| 弯曲强度 Flexural Stress | ISO 178 | ||
| 3.50% 应变，23℃ 3.5% Strain, 23°C | 300 | MPa | ISO 178 |
| 3.50% 应变，100℃ 3.5% Strain, 100°C | 170 | MPa | ISO 178 |
| 3.50% 应变，150℃ 3.5% Strain, 150°C | 123 | MPa | ISO 178 |
| 3.50% 应变，175℃ 3.5% Strain, 175°C | 112 | MPa | ISO 178 |
| 压缩强度 Compressive Strength | 148 | MPa | ASTM D695 |
| 剪切强度 Shear Strength | 87.6 | MPa | ASTM D732 |
| 泊松比 Poisson's Ratio | 0.39 | ASTM E132 | |
| 洛氏硬度 洛氏硬度 | |||
| R 级 R 级 | 125 | ASTM D785 | |