| 牌号简介 About |
|---|
| Amodel HFZ A- 4133 L聚邻苯二甲酰胺（PPA）是一种33％玻纤维增强、热水可成形树脂。主要性能包括耐热性、在宽的温度范围内降低了气体排放、高强度和刚度、低吸湿性、优异的耐化学性和优良的电性能。 Amodel HFZ A- 4133 L树脂是汽车电气、电子产品，包括连接器、插座、开关和传感器等的理想选择。也是发动机罩下用于保护关键控制系统，如防抱死制动系统、牵引力控制系统、转向系统、发动机电子控制、传动和底盘控制单元等外壳的不错选择。 - 黑色：HFZ A-4133 L BK 324 本色： HFZ A-4133 L NT Amodel® HFZ A-4133 L polyphthalamide (PPA) is a 33% glass-reinforced, hot water moldable resin. Key properties include heat resistance, reduced outgassing and high strength and stiffness over a broad temperature range. It also displays low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel® HFZ A-4133 L resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Black: HFZ A-4133 L BK 324 Natural: HFZ A-4133 L NT |
产品描述 Product Description
厂家：比利时索尔维 Solvay Engineering Plastics
类别：PPA PPA
用途：相机应用;电气/电子应用领域;机器/机械部件;连接器;金属取代;手机;草坪和园林设备;汽车领域的应用;工业应用;通用;工业部件;线轴;汽车电子;汽车的发动机罩下的零件;
颜色：黑色,自然色
加工条件：水温模具注塑成型
性能特点：低吸湿性; 防火阻燃等级HB; 机械强度好; 尺寸稳定性好; 成型周期快; 耐化学性; 润滑性; 流动性高; 韧性好; Good Rigidity,Good flexibility,Good Dimensional Stability,High liquidity,Quick molding cycle,Lubricating,Solvent resistance,Low moisture absorption,HB
填料：玻璃纤维 33
| 技术参数 Technical Data | |||
|---|---|---|---|
物理性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 密度 Density | 1.46 | g/cm³ | ISO 1183/A |
| 收缩率 收缩率 | |||
| TD TD | 1.0 | % | ASTM D955 |
| MD MD | 0.50 | % | ASTM D955 |
| 吸水率 吸水率 | |||
| 24hr 24 hr | 0.26 | % | ASTM D570 |
机械性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 拉伸模量 Tensile Modulus | 12000 | MPa | ISO 527-2 |
| 拉伸强度 拉伸强度 | |||
| 断裂 断裂 | 180 | MPa | ISO 527-2 |
| 拉伸应变 拉伸应变 | |||
| 断裂 断裂 | 1.8 | % | ISO 527-2 |
| 弯曲模量 Flexural Modulus | 11000 | MPa | ISO 178 |
| 弯曲强度 Flexural Stress | 255 | MPa | ISO 178 |
冲击性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 简支梁缺口冲击强度 Charpy Notched Impact Strength | 8.2 | kJ/m² | ISO 179-1eA |
| 悬臂梁缺口冲击强度 Notched Izod Impact Strength | 8.4 | kJ/m² | ISO 180-1A |
| 悬臂梁无缺口冲击强度 Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180/1U |
热性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 热变形温度 热变形温度 | |||
| 1.8 MPa，未退火 1.8 MPa，未退火 | 310 | ℃ | ISO 75-2/A |
| 熔融温度 溶融温度 | |||
| DSC DSC | 327 | ℃ | ISO 3146 |
| 线性热膨胀系数 线性热膨胀系数 | |||
| TD TD | ASTM E831 | ||
| 0 到 90℃ 0 to 90°C | 6.3E-5 | cm/cm/℃ | ASTM E831 |
| 150 到 250℃ 150 to 250°C | 1.5E-4 | cm/cm/℃ | ASTM E831 |
| MD MD | ASTM E831 | ||
| 0 到 90℃ 0 to 90°C | 2.0E-5 | cm/cm/℃ | ASTM E831 |
| 150 到 250℃ 150 to 250°C | 1.4E-5 | cm/cm/℃ | ASTM E831 |
电气性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 表面电阻率 Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| 体积电阻率 Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| 介电强度 Electric Strength | 19 | kV/mm | ASTM D149 |
| 介电常数 Dielectric Constant | ASTM D150 | ||
| 60 Hz 60 Hz | 3.90 | ASTM D150 | |
| 1 MHz 1 MHz | 3.70 | ASTM D150 | |
| 耗散因数 Dissipation Factor | ASTM D150 | ||
| 60 Hz 60 Hz | 6.0E-3 | ASTM D150 | |
| 1 MHz 1 MHz | 0.016 | ASTM D150 | |
| 高电弧燃烧指数（HAI） High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| 高压电弧抗点燃指数（HVAR）（PLC） High Voltage Arc Resistance to Ignition (HVAR) | PLC 0 | UL 746 | |
| 高电压电弧起痕速率 高电压电弧起痕速率 | |||
| HVTR HVTR | PLC 0 | UL 746 | |
| 热丝引燃 热丝引燃 | |||
| HWI HWI | PLC 1 | UL 746 | |
阻燃性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 0.80 mm 0.8 mm 2 | HB | UL 94 | |
| 灼热丝可燃性指数 Glow Wire Flammability Index | 800 | ℃ | IEC 60695-2-12 |
| 灼热丝起燃温度 Glow Wire Ignition Temperature | 800 | ℃ | IEC 60695-2-13 |