牌号简介 About |
---|
Texin 990R树脂是一种以聚醚为基础的热塑性聚氨酯,肖氏硬度约为90A,含有一种内释型添加剂。这种树脂可以通过注塑或挤出加工。 Texin 990R resin is a polyether-based thermoplastic polyurethane with a Shore hardness of approximately 90A. It contains an internal mold release additive. This resin can be processed by injection molding or extrusion. |
产品描述 Product Description
厂家:德国科思创 Covestro - PUR
类别:TPU-醚 TPU-醚
用途:电缆护套;鞋类;薄膜;管道;密封件;型材;车轮;垫圈;管件;
颜色:自然色
加工条件:挤出 Extrusion
性能特点:耐磨; 耐水解; 食品接触; 冲击性能好; 韧性好; Good flexibility,High impact resistance,Hydrolysis stability,Food contact compliance,Good wear resistance
技术参数 Technical Data | |||
---|---|---|---|
物理性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
密度 Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
密度 Density | 1.13 | g/cm³ | ISO 1183 |
收缩率 Molding Shrinkage | ISO 2577 | ||
TD:2.54 mm TD,2.54 mm | 0.80 | % | ASTM D955 |
MD:2.54 mm MD,2.54 mm | 0.80 | % | ASTM D955 |
TD:2.54 mm Across Flow : 2.54 mm | 0.80 | % | ISO 2577 |
MD:2.54 mm Flow : 2.54 mm | 0.80 | % | ISO 2577 |
机械性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
邵氏硬度 邵氏硬度 | |||
邵氏 A 邵氏 A | 90 | ASTM D2240 | |
邵氏 A 邵氏 A | 90 | ISO 868 | |
弯曲模量 弯曲模量 | |||
23℃ 23℃ | 41.4 | MPa | ASTM D790 |
23℃ 23℃ | 41.4 | MPa | ISO 178 |
泰伯耐磨性 Taber Abrasion Resistance | |||
1000 周期,1000 g,H-18 转轮 1000 Cycles, 1000 g, H-18 Wheel | 25.0 | mg | ISO 4649 |
1000 周期,1000 g,H-18 转轮 1000 Cycles, 1000 g, H-18 Wheel | 25.0 | mg | ASTM D1044 |
弹性体 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
拉伸强度 Tensile Stress | |||
屈服 屈服 | 41.4 | MPa | ASTM D412 |
屈服 屈服 | 41.4 | MPa | ISO 37 |
300% 应变 300%应变 | 14.5 | MPa | ISO 37 |
300% 应变 300%应变 | 14.5 | MPa | ASTM D412 |
100% 应变 100%应变 | 7.60 | MPa | ISO 37 |
100% 应变 100%应变 | 7.60 | MPa | ASTM D412 |
50% 应变 50% Strain | 6.90 | MPa | ISO 37 |
50% 应变 50% Strain | 6.90 | MPa | ASTM D412 |
拉伸应变 拉伸应变 | |||
断裂 断裂 | 520 | % | ISO 37 |
断裂 断裂 | 520 | % | ASTM D412 |
撕裂强度 Tear Strength 2 2 | 96.3 | kN/m | ASTM D624 |
撕裂强度 Tear Strength | 96 | kN/m | ISO 34-1 |
压缩形变 Compression Set | ASTM D395B | ||
23℃,22 hr 23°C, 22 hr 3 3 | 15 | % | ASTM D395B |
23℃,22 hr 23°C, 22 hr | 20 | % | ASTM D395B |
70℃,22 hr 70°C, 22 hr 3 3 | 35 | % | ASTM D395B |
70℃,22 hr 70°C, 22 hr | 75 | % | ASTM D395B |
压缩形变 Compression Set | ISO 815 | ||
23℃,22 hr 23°C, 22 hr 3 3 | 15 | % | ISO 815 |
23℃,22 hr 23°C, 22 hr | 20 | % | ISO 815 |
70℃,22 hr 70°C, 22 hr | 75 | % | ISO 815 |
70℃,22 hr 70°C, 22 hr 3 3 | 35 | % | ISO 815 |
巴肖氏弹性 Bayshore Resilience | 40 | % | ASTM D2632 |
热性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
脆化温度 Brittleness Temperature | < -68.0 | ℃ | ASTM D746 |
脆化温度 Brittleness Temperature | < -68.0 | ℃ | ISO 974 |
玻璃化转变温度 Glass Transition Temperature | -44.0 | ℃ | DMA |
维卡软化温度 Vicat Softening Temperature | 106 | ℃ | ASTM D1525 4 |
维卡软化温度 Vicat Softening Temperature | 106 | ℃ | ISO 306/50 |
老化性能 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
空气中拉伸强度的变化率 Change in Tensile Strength in Air | ASTM D573 | ||
100℃,70 hr 100°C, 70 hr | 16 | % | ASTM D573 |
100% Strain,100℃,70 hr 100% Strain, 100°C, 70 hr | 5.0 | % | ASTM D573 |
300% Strain,100℃,70 hr 300% Strain, 100°C, 70 hr | 3.0 | % | ASTM D573 |
100℃,168 hr 100°C, 168 hr | 24 | % | ASTM D573 |
100% Strain,100℃,168 hr 100% Strain, 100°C, 168 hr | 6.0 | % | ASTM D573 |
300% Strain,100℃,168 hr 300% Strain, 100°C, 168 hr | 1.0 | % | ASTM D573 |
100℃,336 hr 100°C, 336 hr | 27 | % | ASTM D573 |
100% Strain,100℃,336 hr 100% Strain, 100°C, 336 hr | 7.0 | % | ASTM D573 |
300% Strain,100℃,336 hr 300% Strain, 100°C, 336 hr | -9.0 | % | ASTM D573 |
100℃,504 hr 100°C, 504 hr | -9.0 | % | ASTM D573 |
100% Strain,100℃,504 hr 100% Strain, 100°C, 504 hr | -3.0 | % | ASTM D573 |
300% Strain,100℃,504 hr 300% Strain, 100°C, 504 hr | -24 | % | ASTM D573 |
空气中拉伸强度的变化率 Change in Tensile Strength in Air | ISO 216 | ||
100℃,70 hr 100°C, 70 hr | 16 | % | ISO 216 |
100% Strain 100℃,70 hr 100% Strain 100°C, 70 hr | 5.0 | % | ISO 216 |
300% Strain 100℃,70 hr 300% Strain 100°C, 70 hr | 3.0 | % | ISO 216 |
100℃,168 hr 100°C, 168 hr | 24 | % | ISO 216 |
100% Strain 100℃,168 hr 100% Strain 100°C, 168 hr | 6.0 | % | ISO 216 |
300% Strain 100℃,168 hr 300% Strain 100°C, 168 hr | 1.0 | % | ISO 216 |
100℃,336 hr 100°C, 336 hr | 27 | % | ISO 216 |
100% Strain 100℃,336 hr 100% Strain 100°C, 336 hr | 7.0 | % | ISO 216 |
300% Strain 100℃,336 hr 300% Strain 100°C, 336 hr | -9.0 | % | ISO 216 |
100℃,504 hr 100°C, 504 hr | -9.0 | % | ISO 216 |
100% Strain 100℃,504 hr 100% Strain 100°C, 504 hr | -3.0 | % | ISO 216 |
300% Strain 100℃,504 hr 300% Strain 100°C, 504 hr | -24 | % | ISO 216 |
空气中极限伸长率的变化率 Change in Ultimate Elongation in Air | ASTM D573 | ||
100℃,70 hr 100°C, 70 hr | 16 | % | ASTM D573 |
100℃,168 hr 100°C, 168 hr | 20 | % | ASTM D573 |
100℃,336 hr 100°C, 336 hr | 36 | % | ASTM D573 |
100℃,504 hr 100°C, 504 hr | 68 | % | ASTM D573 |
在空气中断裂时拉伸应力变化 Change in Tensile Strain at Break in Air | ISO 216 | ||
100℃,70 hr 100°C, 70 hr | 16 | % | ISO 216 |
100℃,168 hr 100°C, 168 hr | 20 | % | ISO 216 |
100℃,336 hr 100°C, 336 hr | 36 | % | ISO 216 |
100℃,504 hr 100°C, 504 hr | 68 | % | ISO 216 |
空气中硬度计硬度的变化率 Change in Durometer Hardness in Air | ASTM D573 | ||
邵氏 D,100℃,70 hr Shore D, 100°C, 70 hr | 2.0 | ASTM D573 | |
邵氏 D,100℃,168 hr Shore D, 100°C, 168 hr | 1.0 | ASTM D573 | |
邵氏 D,100℃,336 hr Shore D, 100°C, 336 hr | 0.0 | ASTM D573 | |
邵氏 D,100℃,504 hr Shore D, 100°C, 504 hr | 0.0 | ASTM D573 | |
空气中邵氏硬度的变化率 Change in Shore Hardness in Air | ISO 216 | ||
邵氏 D,100℃,70 hr Shore D, 100°C, 70 hr | 2.0 | ISO 216 | |
邵氏 D,100℃,168 hr Shore D, 100°C, 168 hr | 1.0 | ISO 216 | |
邵氏 D,100℃,336 hr Shore D, 100°C, 336 hr | 0.0 | ISO 216 | |
邵氏 D,100℃,504 hr Shore D, 100°C, 504 hr | 0.0 | ISO 216 | |
拉伸强度的变化率 Change in Tensile Strength | ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23°C, 70 hr, in Reference Fuel A (Isooctane) | 12 | % | ASTM D471 |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain, 23°C, 70 hr, in Reference Fuel A (Isooctane) | -5.0 | % | ASTM D471 |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain, 23°C, 70 hr, in Reference Fuel A (Isooctane) | -6.0 | % | ASTM D471 |
23℃,70 hr,甲醇 73°F, 70 hr, in Reference Fuel C | -28 | % | ASTM D471 |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain, 23°C, 70 hr, in Reference Fuel C | -23 | % | ASTM D471 |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain, 23°C, 70 hr, in Reference Fuel C | -22 | % | ASTM D471 |
23℃,168 hr,in Reference Fuel A(Isooctane) 23°C, 168 hr, in Reference Fuel A (Isooctane) | 12 | % | ASTM D471 |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain, 23°C, 168 hr, in Reference Fuel A (Isooctane) | -1.0 | % | ASTM D471 |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain, 23°C, 168 hr, in Reference Fuel A (Isooctane) | -6.0 | % | ASTM D471 |
23℃,168 hr,甲醇 73°F, 168 hr, in Reference Fuel C | -25 | % | ASTM D471 |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain, 23°C, 168 hr, in Reference Fuel C | -20 | % | ASTM D471 |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain, 23°C, 168 hr, in Reference Fuel C | -19 | % | ASTM D471 |
23℃,336 hr,in Reference Fuel A(Isooctane) 23°C, 336 hr, in Reference Fuel A (Isooctane) | 7.0 | % | ASTM D471 |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain, 23°C, 336 hr, in Reference Fuel A (Isooctane) | -4.0 | % | ASTM D471 |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain, 23°C, 336 hr, in Reference Fuel A (Isooctane) | -10 | % | ASTM D471 |
23℃,336 hr,in Reference Fuel C 23°C, 336 hr, in Reference Fuel C | -27 | % | ASTM D471 |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain, 23°C, 336 hr, in Reference Fuel C | -19 | % | ASTM D471 |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain, 23°C, 336 hr, in Reference Fuel C | -19 | % | ASTM D471 |
23℃,504 hr,in Reference Fuel A(Isooctane) 23°C, 504 hr, in Reference Fuel A (Isooctane) | 19 | % | ASTM D471 |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain, 23°C, 504 hr, in Reference Fuel A (Isooctane) | -1.0 | % | ASTM D471 |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain, 23°C, 504 hr, in Reference Fuel A (Isooctane) | -3.0 | % | ASTM D471 |
23℃,504 hr,in Reference Fuel C 23°C, 504 hr, in Reference Fuel C | -28 | % | ASTM D471 |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain, 23°C, 504 hr, in Reference Fuel C | -16 | % | ASTM D471 |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain, 23°C, 504 hr, in Reference Fuel C | -18 | % | ASTM D471 |
100℃,70 hr,在ASTM #1油中 212°F, 70 hr, in ASTM #1 Oil | 15 | % | ASTM D471 |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain, 100°C, 70 hr, in ASTM #1 Oil | 2.0 | % | ASTM D471 |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain, 100°C, 70 hr, in ASTM #1 Oil | -1.0 | % | ASTM D471 |
100℃,70 hr,在ASTM #3油中 212°F, 70 hr, in ASTM #3 Oil | 22 | % | ASTM D471 |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain, 100°C, 70 hr, in ASTM #3 Oil | 2.0 | % | ASTM D471 |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain, 100°C, 70 hr, in ASTM #3 Oil | -1.0 | % | ASTM D471 |
100℃,168 hr,in ASTM #1 Oil 100°C, 168 hr, in ASTM #1 Oil | -10 | % | ASTM D471 |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain, 100°C, 168 hr, in ASTM #1 Oil | 4.0 | % | ASTM D471 |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain, 100°C, 168 hr, in ASTM #1 Oil | 14 | % | ASTM D471 |
100℃,168 hr,in ASTM #3 Oil 100°C, 168 hr, in ASTM #3 Oil | 15 | % | ASTM D471 |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain, 100°C, 168 hr, in ASTM #3 Oil | 4.0 | % | ASTM D471 |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain, 100°C, 168 hr, in ASTM #3 Oil | 14 | % | ASTM D471 |
100℃,336 hr,in ASTM #1 Oil 100°C, 336 hr, in ASTM #1 Oil | -4.0 | % | ASTM D471 |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain, 100°C, 336 hr, in ASTM #1 Oil | 8.0 | % | ASTM D471 |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain, 100°C, 336 hr, in ASTM #1 Oil | 1.0 | % | ASTM D471 |
100℃,336 hr,in ASTM #3 Oil 100°C, 336 hr, in ASTM #3 Oil | 5.0 | % | ASTM D471 |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain, 100°C, 336 hr, in ASTM #3 Oil | 8.0 | % | ASTM D471 |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain, 100°C, 336 hr, in ASTM #3 Oil | 1.0 | % | ASTM D471 |
100℃,504 hr,in ASTM #1 Oil 100°C, 504 hr, in ASTM #1 Oil | -12 | % | ASTM D471 |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain, 100°C, 504 hr, in ASTM #1 Oil | 6.0 | % | ASTM D471 |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain, 100°C, 504 hr, in ASTM #1 Oil | 3.0 | % | ASTM D471 |
100℃,504 hr,in ASTM #3 Oil 100°C, 504 hr, in ASTM #3 Oil | -2.0 | % | ASTM D471 |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain, 100°C, 504 hr, in ASTM #3 Oil | 6.0 | % | ASTM D471 |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain, 100°C, 504 hr, in ASTM #3 Oil | 3.0 | % | ASTM D471 |
拉伸强度的变化率 Change in Tensile Strength | ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23°C, 70 hr, in Reference Fuel A (Isooctane) | 12 | % | ISO 175 |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain, 23°C, 70 hr, in Reference Fuel A (Isooctane) | -5.0 | % | ISO 175 |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain, 23°C, 70 hr, in Reference Fuel A (Isooctane) | -6.0 | % | ISO 175 |
23℃,70 hr,甲醇 73°F, 70 hr, in Reference Fuel C | -28 | % | ISO 175 |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain, 23°C, 70 hr, in Reference Fuel C | -23 | % | ISO 175 |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain, 23°C, 70 hr, in Reference Fuel C | -22 | % | ISO 175 |
23℃,168 hr,in Reference Fuel A(Isooctane) 23°C, 168 hr, in Reference Fuel A (Isooctane) | 12 | % | ISO 175 |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain, 23°C, 168 hr, in Reference Fuel A (Isooctane) | -1.0 | % | ISO 175 |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain, 23°C, 168 hr, in Reference Fuel A (Isooctane) | -6.0 | % | ISO 175 |
23℃,168 hr,甲醇 73°F, 168 hr, in Reference Fuel C | -25 | % | ISO 175 |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain, 23°C, 168 hr, in Reference Fuel C | -20 | % | ISO 175 |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain, 23°C, 168 hr, in Reference Fuel C | -19 | % | ISO 175 |
23℃,336 hr,in Reference Fuel A(Isooctane) 23°C, 336 hr, in Reference Fuel A (Isooctane) | 7.0 | % | ISO 175 |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain, 23°C, 336 hr, in Reference Fuel A (Isooctane) | -4.0 | % | ISO 175 |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain, 23°C, 336 hr, in Reference Fuel A (Isooctane) | -10 | % | ISO 175 |
23℃,336 hr,in Reference Fuel C 23°C, 336 hr, in Reference Fuel C | -27 | % | ISO 175 |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain, 23°C, 336 hr, in Reference Fuel C | -19 | % | ISO 175 |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain, 23°C, 336 hr, in Reference Fuel C | -19 | % | ISO 175 |
23℃,504 hr,in Reference Fuel A(Isooctane) 23°C, 504 hr, in Reference Fuel A (Isooctane) | 19 | % | ISO 175 |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain, 23°C, 504 hr, in Reference Fuel A (Isooctane) | -1.0 | % | ISO 175 |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain, 23°C, 504 hr, in Reference Fuel A (Isooctane) | -3.0 | % | ISO 175 |
23℃,504 hr,in Reference Fuel C 23°C, 504 hr, in Reference Fuel C | -28 | % | ISO 175 |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain, 23°C, 504 hr, in Reference Fuel C | -16 | % | ISO 175 |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain, 23°C, 504 hr, in Reference Fuel C | -18 | % | ISO 175 |
100℃,70 hr,在ASTM #1油中 212°F, 70 hr, in ASTM #1 Oil | 15 | % | ISO 175 |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain, 100°C, 70 hr, in ASTM #1 Oil | 2.0 | % | ISO 175 |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain, 100°C, 70 hr, in ASTM #1 Oil | -1.0 | % | ISO 175 |
100℃,70 hr,在ASTM #3油中 212°F, 70 hr, in ASTM #3 Oil | 22 | % | ISO 175 |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain, 100°C, 70 hr, in ASTM #3 Oil | 2.0 | % | ISO 175 |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain, 100°C, 70 hr, in ASTM #3 Oil | -1.0 | % | ISO 175 |
100℃,168 hr,in ASTM #1 Oil 100°C, 168 hr, in ASTM #1 Oil | -10 | % | ISO 175 |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain, 100°C, 168 hr, in ASTM #1 Oil | 4.0 | % | ISO 175 |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain, 100°C, 168 hr, in ASTM #1 Oil | 14 | % | ISO 175 |
100℃,168 hr,in ASTM #3 Oil 100°C, 168 hr, in ASTM #3 Oil | 15 | % | ISO 175 |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain, 100°C, 168 hr, in ASTM #3 Oil | 4.0 | % | ISO 175 |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain, 100°C, 168 hr, in ASTM #3 Oil | 14 | % | ISO 175 |
100℃,336 hr,in ASTM #1 Oil 100°C, 336 hr, in ASTM #1 Oil | -4.0 | % | ISO 175 |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain, 100°C, 336 hr, in ASTM #1 Oil | 8.0 | % | ISO 175 |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain, 100°C, 336 hr, in ASTM #1 Oil | 1.0 | % | ISO 175 |
100℃,336 hr,in ASTM #3 Oil 100°C, 336 hr, in ASTM #3 Oil | 5.0 | % | ISO 175 |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain, 100°C, 336 hr, in ASTM #3 Oil | 8.0 | % | ISO 175 |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain, 100°C, 336 hr, in ASTM #3 Oil | 1.0 | % | ISO 175 |
100℃,504 hr,in ASTM #1 Oil 100°C, 504 hr, in ASTM #1 Oil | -12 | % | ISO 175 |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain, 100°C, 504 hr, in ASTM #1 Oil | 6.0 | % | ISO 175 |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain, 100°C, 504 hr, in ASTM #1 Oil | 3.0 | % | ISO 175 |
100℃,504 hr,in ASTM #3 Oil 100°C, 504 hr, in ASTM #3 Oil | -2.0 | % | ISO 175 |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain, 100°C, 504 hr, in ASTM #3 Oil | 6.0 | % | ISO 175 |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain, 100°C, 504 hr, in ASTM #3 Oil | 3.0 | % | ISO 175 |
极限伸长率的变化率 Change in Ultimate Elongation | ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23°C, 70 hr, in Reference Fuel A (Isooctane) | 11 | % | ASTM D471 |
23℃,70 hr,甲醇 73°F, 70 hr, in Reference Fuel C | 4.0 | % | ASTM D471 |
23℃,168 hr,in Reference Fuel A(Isooctane) 23°C, 168 hr, in Reference Fuel A (Isooctane) | 0.0 | % | ASTM D471 |
23℃,168 hr,甲醇 73°F, 168 hr, in Reference Fuel C | 3.0 | % | ASTM D471 |
23℃,336 hr,in Reference Fuel A(Isooctane) 23°C, 336 hr, in Reference Fuel A (Isooctane) | 15 | % | ASTM D471 |
23℃,336 hr,in Reference Fuel C 23°C, 336 hr, in Reference Fuel C | 5.0 | % | ASTM D471 |
23℃,504 hr,in Reference Fuel A(Isooctane) 23°C, 504 hr, in Reference Fuel A (Isooctane) | 7.0 | % | ASTM D471 |
23℃,504 hr,in Reference Fuel C 23°C, 504 hr, in Reference Fuel C | 3.0 | % | ASTM D471 |
100℃,70 hr,在ASTM #1油中 212°F, 70 hr, in ASTM #1 Oil | 28 | % | ASTM D471 |
100℃,70 hr,在ASTM #3油中 212°F, 70 hr, in ASTM #3 Oil | 28 | % | ASTM D471 |
100℃,168 hr,in ASTM #1 Oil 100°C, 168 hr, in ASTM #1 Oil | 30 | % | ASTM D471 |
100℃,168 hr,in ASTM #3 Oil 100°C, 168 hr, in ASTM #3 Oil | 30 | % | ASTM D471 |
100℃,336 hr,in ASTM #1 Oil 100°C, 336 hr, in ASTM #1 Oil | 31 | % | ASTM D471 |
100℃,336 hr,in ASTM #3 Oil 100°C, 336 hr, in ASTM #3 Oil | 31 | % | ASTM D471 |
100℃,504 hr,in ASTM #1 Oil 100°C, 504 hr, in ASTM #1 Oil | 33 | % | ASTM D471 |
100℃,504 hr,in ASTM #3 Oil 100°C, 504 hr, in ASTM #3 Oil | 33 | % | ASTM D471 |
断裂时拉伸应力变化 Change in Tensile Strain at Break | ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23°C, 70 hr, in Reference Fuel A (Isooctane) | 11 | % | ISO 175 |
23℃,70 hr,甲醇 73°F, 70 hr, in Reference Fuel C | 4.0 | % | ISO 175 |
23℃,168 hr,in Reference Fuel A(Isooctane) 23°C, 168 hr, in Reference Fuel A (Isooctane) | 0.0 | % | ISO 175 |
23℃,168 hr,甲醇 73°F, 168 hr, in Reference Fuel C | 3.0 | % | ISO 175 |
23℃,336 hr,in Reference Fuel A(Isooctane) 23°C, 336 hr, in Reference Fuel A (Isooctane) | 15 | % | ISO 175 |
23℃,336 hr,in Reference Fuel C 23°C, 336 hr, in Reference Fuel C | 5.0 | % | ISO 175 |
23℃,504 hr,in Reference Fuel A(Isooctane) 23°C, 504 hr, in Reference Fuel A (Isooctane) | 7.0 | % | ISO 175 |
23℃,504 hr,in Reference Fuel C 23°C, 504 hr, in Reference Fuel C | 3.0 | % | ISO 175 |
100℃,70 hr,在ASTM #1油中 212°F, 70 hr, in ASTM #1 Oil | 28 | % | ISO 175 |
100℃,70 hr,在ASTM #3油中 212°F, 70 hr, in ASTM #3 Oil | 28 | % | ISO 175 |
100℃,168 hr,in ASTM #1 Oil 100°C, 168 hr, in ASTM #1 Oil | 30 | % | ISO 175 |
100℃,168 hr,in ASTM #3 Oil 100°C, 168 hr, in ASTM #3 Oil | 30 | % | ISO 175 |
100℃,336 hr,in ASTM #1 Oil 100°C, 336 hr, in ASTM #1 Oil | 31 | % | ISO 175 |
100℃,336 hr,in ASTM #3 Oil 100°C, 336 hr, in ASTM #3 Oil | 31 | % | ISO 175 |
100℃,504 hr,in ASTM #1 Oil 100°C, 504 hr, in ASTM #1 Oil | 33 | % | ISO 175 |
100℃,504 hr,in ASTM #3 Oil 100°C, 504 hr, in ASTM #3 Oil | 33 | % | ISO 175 |
邵氏硬度的变化率 Change in Durometer Hardness 6 2 | ASTM D471 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23°C, 70 hr, in Reference Fuel A (Isooctane) | 1.0 | ASTM D471 | |
邵氏 D,23℃,70 hr,在基准燃料C中 Shore D, 23°C, 70 hr, in Reference Fuel C | -4.0 | ASTM D471 | |
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23°C, 168 hr, in Reference Fuel A (Isooctane) | 0.0 | ASTM D471 | |
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23°C, 168 hr, in Reference Fuel C | -4.0 | ASTM D471 | |
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23°C, 336 hr, in Reference Fuel A (Isooctane) | 2.0 | ASTM D471 | |
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23°C, 336 hr, in Reference Fuel C | -4.0 | ASTM D471 | |
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23°C, 504 hr, in Reference Fuel A (Isooctane) | 0.0 | ASTM D471 | |
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23°C, 504 hr, in Reference Fuel C | -3.0 | ASTM D471 | |
邵氏 D,100℃,70 hr,在ASTM #1油中 Shore D, 100°C, 70 hr, in ASTM #1 Oil | -5.0 | ASTM D471 | |
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100°C, 70 hr, in ASTM #3 Oil | -5.0 | ASTM D471 | |
邵氏 D,100℃,168 hr,在ASTM #1油中 Shore D, 100°C, 168 hr, in ASTM #1 Oil | -4.0 | ASTM D471 | |
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100°C, 168 hr, in ASTM #3 Oil | -4.0 | ASTM D471 | |
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100°C, 336 hr, in ASTM #1 Oil | -3.0 | ASTM D471 | |
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100°C, 336 hr, in ASTM #3 Oil | -3.0 | ASTM D471 | |
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100°C, 504 hr, in ASTM #1 Oil | -2.0 | ASTM D471 | |
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100°C, 504 hr, in ASTM #3 Oil | -2.0 | ASTM D471 | |
邵氏硬度的变化率 Change in Shore Hardness | ISO 175 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23°C, 70 hr, in Reference Fuel A (Isooctane) | 1.0 | ISO 175 | |
邵氏 D,23℃,70 hr,在基准燃料C中 Shore D, 23°C, 70 hr, in Reference Fuel C | -4.0 | ISO 175 | |
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23°C, 168 hr, in Reference Fuel A (Isooctane) | 0.0 | ISO 175 | |
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23°C, 168 hr, in Reference Fuel C | -4.0 | ISO 175 | |
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23°C, 336 hr, in Reference Fuel A (Isooctane) | 2.0 | ISO 175 | |
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23°C, 336 hr, in Reference Fuel C | -4.0 | ISO 175 | |
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23°C, 504 hr, in Reference Fuel A (Isooctane) | 0.0 | ISO 175 | |
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23°C, 504 hr, in Reference Fuel C | -3.0 | ISO 175 | |
邵氏 D,100℃,70 hr,在ASTM #1油中 Shore D, 100°C, 70 hr, in ASTM #1 Oil | -5.0 | ISO 175 | |
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100°C, 70 hr, in ASTM #3 Oil | -5.0 | ISO 175 | |
邵氏 D,100℃,168 hr,在ASTM #1油中 Shore D, 100°C, 168 hr, in ASTM #1 Oil | -4.0 | ISO 175 | |
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100°C, 168 hr, in ASTM #3 Oil | -4.0 | ISO 175 | |
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100°C, 336 hr, in ASTM #1 Oil | -3.0 | ISO 175 | |
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100°C, 336 hr, in ASTM #3 Oil | -3.0 | ISO 175 | |
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100°C, 504 hr, in ASTM #1 Oil | -2.0 | ISO 175 | |
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100°C, 504 hr, in ASTM #3 Oil | -2.0 | ISO 175 | |
体积变化 Change in Volume | ASTM D471 | ||
23℃,70 hr,in Reference Fuel A 23°C, 70 hr, in Reference Fuel A | 2.0 | % | ASTM D471 |
23℃,70 hr,甲醇 73°F, 70 hr, in Reference Fuel C | 35 | % | ASTM D471 |
23℃,168 hr,in Reference Fuel A 23°C, 168 hr, in Reference Fuel A | 3.0 | % | ASTM D471 |
23℃,168 hr,甲醇 73°F, 168 hr, in Reference Fuel C | 35 | % | ASTM D471 |
23℃,336 hr,in Reference Fuel A 23°C, 336 hr, in Reference Fuel A | 4.0 | % | ASTM D471 |
23℃,336 hr,in Reference Fuel C 23°C, 336 hr, in Reference Fuel C | 36 | % | ASTM D471 |
23℃,504 hr,in Reference Fuel A 23°C, 504 hr, in Reference Fuel A | 4.0 | % | ASTM D471 |
23℃,504 hr,in Reference Fuel C 23°C, 504 hr, in Reference Fuel C | 36 | % | ASTM D471 |
100℃,70 hr,在ASTM #1油中 212°F, 70 hr, in ASTM #1 Oil | 0.0 | % | ASTM D471 |
100℃,70 hr,在ASTM #3油中 212°F, 70 hr, in ASTM #3 Oil | 0.0 | % | ASTM D471 |
100℃,168 hr,in ASTM #1 Oil 100°C, 168 hr, in ASTM #1 Oil | 0.0 | % | ASTM D471 |
100℃,168 hr,in ASTM #3 Oil 100°C, 168 hr, in ASTM #3 Oil | 0.0 | % | ASTM D471 |
100℃,336 hr,in ASTM #1 Oil 100°C, 336 hr, in ASTM #1 Oil | 1.0 | % | ASTM D471 |
100℃,336 hr,in ASTM #3 Oil 100°C, 336 hr, in ASTM #3 Oil | 1.0 | % | ASTM D471 |
100℃,504 hr,in ASTM #1 Oil 100°C, 504 hr, in ASTM #1 Oil | 1.0 | % | ASTM D471 |
100℃,504 hr,in ASTM #3 Oil 100°C, 504 hr, in ASTM #3 Oil | 1.0 | % | ASTM D471 |
体积变化 Change in Volume | ISO 175 | ||
23℃,70 hr,in Reference Fuel A 23°C, 70 hr, in Reference Fuel A | 2.0 | % | ISO 175 |
23℃,70 hr,甲醇 73°F, 70 hr, in Reference Fuel C | 35 | % | ISO 175 |
23℃,168 hr,in Reference Fuel A 23°C, 168 hr, in Reference Fuel A | 3.0 | % | ISO 175 |
23℃,168 hr,甲醇 73°F, 168 hr, in Reference Fuel C | 35 | % | ISO 175 |
23℃,336 hr,in Reference Fuel A 23°C, 336 hr, in Reference Fuel A | 4.0 | % | ISO 175 |
23℃,336 hr,in Reference Fuel C 23°C, 336 hr, in Reference Fuel C | 36 | % | ISO 175 |
23℃,504 hr,in Reference Fuel A 23°C, 504 hr, in Reference Fuel A | 4.0 | % | ISO 175 |
23℃,504 hr,in Reference Fuel C 23°C, 504 hr, in Reference Fuel C | 36 | % | ISO 175 |
100℃,70 hr,在ASTM #1油中 212°F, 70 hr, in ASTM #1 Oil | 0.0 | % | ISO 175 |
100℃,70 hr,在ASTM #3油中 212°F, 70 hr, in ASTM #3 Oil | 0.0 | % | ISO 175 |
100℃,168 hr,in ASTM #1 Oil 100°C, 168 hr, in ASTM #1 Oil | 0.0 | % | ISO 175 |
100℃,168 hr,in ASTM #3 Oil 100°C, 168 hr, in ASTM #3 Oil | 0.0 | % | ISO 175 |
100℃,336 hr,in ASTM #1 Oil 100°C, 336 hr, in ASTM #1 Oil | 1.0 | % | ISO 175 |
100℃,336 hr,in ASTM #3 Oil 100°C, 336 hr, in ASTM #3 Oil | 1.0 | % | ISO 175 |
100℃,504 hr,in ASTM #1 Oil 100°C, 504 hr, in ASTM #1 Oil | 1.0 | % | ISO 175 |
100℃,504 hr,in ASTM #3 Oil 100°C, 504 hr, in ASTM #3 Oil | 1.0 | % | ISO 175 |
补充信息 | 额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
压缩载荷 Compressive Load | ASTM D575 | ||
10% 挠曲 10% Deflection | 3.10 | MPa | ASTM D575 |
15% 挠曲 15% Deflection | 4.48 | MPa | ASTM D575 |
2% 挠曲 2% Deflection | 0.689 | MPa | ASTM D575 |
20% 挠曲 20% Deflection | 5.86 | MPa | ASTM D575 |
25% 挠曲 25% Deflection | 7.24 | MPa | ASTM D575 |
5% 挠曲 5% Deflection | 1.72 | MPa | ASTM D575 |
50% 挠曲 50% Deflection | 19.3 | MPa | ASTM D575 |